Property | Test | Typical value | Units |
---|---|---|---|
Melt Flow Index (MFI) | ISO 1133 (190 °C / 2,16 kg) | 14 - 16 | g/10 min |
Density | ISO 1183 | 0,92 - 0,94 | g/cm3 |
Shore D hardness | ISO 868 | 61 - 63 | - |
Property | Test | Typical value | Units |
---|---|---|---|
Tensile Modulus | ISO 527-2/1A/1 | 1.100 - 1.200 | MPa |
Resistance at the tensile yield point | ISO 527-2/1A/50 | 24 - 26 | MPa |
Elongation at break to traction | ISO 527-2/1A/50 | >30 | % |
Impact resistance Charpy with notch (23ºC) | ISO 179-1/1eA | 2 - 3 | kJ/m2 |
- Todas las propiedades, salvo el MFI, están determinadas sobre probetas ISO tipo 1-A obtenidas por moldeo por inyección.
- Los Valores Típicos son valores medios representativos.
Disclaimer:
Este producto es un material reciclado. Aunque las materias primas empleadas presentan homogeneidad y regularidad, las propiedades y/o el comportamiento del material pueden variar. Así, los valores indicados en esta ficha técnica no deben tomarse como especificaciones. Son proporcionadas de buena fe, si bien Polymer Recycling Labs, S.L. no ofrece garantías ni asumirá ninguna responsabilidad por la información contenida en este documento, que es válida y fidedigna a partir de la fecha de publicación.
La responsabilidad referente a la seguridad y a la legalidad del uso, el manejo y el procesamiento de este material recae sobre el Comprador, quien será igualmente responsable de determinar si el material y la información contenida en esta ficha son apropiados para la aplicación en la que el Comprador lo utilice.
Property | Test | Typical value | Units |
---|---|---|---|
Melt Flow Index (MFI) | ISO 1133 (190 °C / 2,16 kg) | 4-5 | g/10 min |
Density | ISO 1183 | 0,94 - 0,96 | g/cm3 |
Shore D hardness | ISO 868 | 60 - 62 | - |
Property | Test | Typical value | Units |
---|---|---|---|
Tensile Modulus | ISO 527-2/1A-1 | 900-1000 | MPa |
Resistance at the tensile yield point | ISO 527-2/1A/1 | 20-22 | MPa |
Elongation at break to traction | ISO 527-2/1A/50 | >30 | % |
Impact resistance Charpy with notch (23ºC) | ISO 179-1/1eA | >4 | kJ/m2 |
- All properties, except MFI tests, are conducted on ISO type 1-A injection moulded test specimens.
- Typical Values are representative mean values.
Disclaimer:
This product is a recycled grade. Although raw materials are regular and homogeneous, material properties and/or performance may vary. Hence, values indicated in this datasheet are not to be construed as specifications. They are provided in good faith, but no guarantees are given and no responsibility is assumed by Polymer Recycling Labs, S.L. for the information in this document, which is accurate and reliable as of the date of publication.
The responsibility for safe and legal use, handling and processing of this material relies on the Customer, who is also responsible for determining whether the material and the information in this document are appropriate for the Customer’s use.
© 2018 POLYMER RECYCING LABS, S.L.
Property | Test | Typical value | Units |
---|---|---|---|
Melt Flow Index (MFI) | ISO 1133 (190 °C / 2,16 kg) | 9 - 11 | g/10 min |
Density | ISO 1183 | 0,91 - 0,92 | g/cm3 |
Shore D hardness | ISO 868 | 61 - 63 | - |
Property | Test | Typical value | Units |
---|---|---|---|
Tensile Modulus | ISO 527‐2/1A/1 | 1050 - 1150 | MPa |
Resistance at the tensile yield point | ISO 527-2/1A/50 | 23 - 25 | MPa |
Elongation at break to traction | ISO 527-2/1A/50 | >30 | % |
Impact resistance Charpy with notch (23ºC) | ISO 179-1/1eA | >5 | kJ/m2 |
- All properties, except MFI tests, are conducted on ISO type 1-A injection moulded test specimens.
- Typical Values are representative mean values.
This product is a recycled grade. Although raw materials are regular and homogeneous, material properties and/or performance may vary. Hence, values indicated in this datasheet are not to be construed as specifications. They are provided in good faith, but no guarantees are given and no responsibility is assumed by Polymer Recycling Labs, S.L. for the information in this document, which is accurate and reliable as of the date of publication.
The responsibility for safe and legal use, handling and processing of this material relies on the Customer, who is also responsible for determining whether the material and the information in this document are appropriate for the Customer’s use.
Property | Test | Typical value | Units |
---|---|---|---|
Melt Flow Index (MFI) | ISO 1133 (190 ºC / 2,16 kg) | 12 - 14 | g/10 min |
Density | ISO 1183 | 0,93 - 0,94 | g/cm3 |
Shore D hardness | ISO 868 | 60 - 62 | - |
Property | Test | Typical value | Units |
---|---|---|---|
Tensile Modulus | ISO 527‐2/1A/1 | 1.100 - 1.200 | MPa |
Resistance at the tensile yield point | ISO 527-2/1A/50 | 21 - 23 | MPa |
Elongation at break to traction | ISO 527-2/1A/50 | >30 | % |
Impact resistance Charpy with notch (23ºC) | ISO 179-1/1eA | >6 | kJ/m2 |
- All properties, except MFI tests, are conducted on ISO type 1-A injection moulded test specimens.
- Typical Values are representative mean values.
Disclaimer:
This product is a recycled grade. Although raw materials are regular and homogeneous, material properties and/or performance may vary. Hence, values indicated in this datasheet are not to be construed as specifications. They are provided in good faith, but no guarantees are given and no responsibility is assumed by Polymer Recycling Labs, S.L. for the information in this document, which is accurate and reliable as of the date of publication.
The responsibility for safe and legal use, handling and processing of this material relies on the Customer, who is also responsible for determining whether the material and the information in this document are appropriate for the Customer’s use.
© 2018 POLYMER RECYCING LABS, S.L.
Property | Test | Typical value | Units |
---|---|---|---|
Melt Flow Index (MFI) | ISO 1133 (190 ºC / 2,16 kg) | 10 - 12 | g/10 min |
Density | ISO 1183 | 0,95 - 0,97 | g/cm3 |
Shore D hardness | ISO 868 | 56 - 58 | - |
Property | Test | Typical value | Units |
---|---|---|---|
Tensile Modulus | ISO 527‐2/1A/1 | 1.150 - 1.250 | MPa |
Resistance at the tensile yield point | ISO 527‐2/1A/50 | 18 | MPa |
Elongation at break to traction | |||
Impact resistance Charpy with notch (23ºC) | ISO 179-1/1eA | > 30 | kJ/m2 |
- All properties, except MFI tests, are conducted on ISO type 1-A injection moulded test specimens.
- Typical Values are representative mean values.
Disclaimer:
This product is a recycled grade. Although raw materials are regular and homogeneous, material properties and/or performance may vary. Hence, values indicated in this datasheet are not to be construed as specifications. They are provided in good faith, but no guarantees are given and no responsibility is assumed by Polymer Recycling Labs, S.L. for the information in this document, which is accurate and reliable as of the date of publication.
The responsibility for safe and legal use, handling and processing of this material relies on the Customer, who is also responsible for determining whether the material and the information in this document are appropriate for the Customer’s use.
Property | Test | Typical value | Units |
---|---|---|---|
Melt Flow Index (MFI) | ISO 1133 (190ºC / 2,16 kg) | 18 - 20 | g/10 min |
Density | ISO 1183 | 0,91 - 0,93 | g/cm3 |
Shore D hardness | ISO 868 | 63 - 65 | - |
Property | Test | Typical value | Units |
---|---|---|---|
Tensile Modulus | ISO 527‐2/1A/1 | 1.100 - 1.200 | MPa |
Resistance at the tensile yield point | ISO 527-2/1A/50 | 24 - 26 | MPa |
Elongation at break to traction | |||
Impact resistance Charpy with notch (23ºC) | ISO 179-1/1eA | > 3 | kJ/m2 |
- All properties, except MFI tests, are conducted on ISO type 1-A injection moulded test specimens.
- Typical Values are representative mean values.
Disclaimer:
This product is a recycled grade. Although raw materials are regular and homogeneous, material properties and/or performance may vary. Hence, values indicated in this datasheet are not to be construed as specifications. They are provided in good faith, but no guarantees are given and no responsibility is assumed by Polymer Recycling Labs, S.L. for the information in this document, which is accurate and reliable as of the date of publication.
The responsibility for safe and legal use, handling and processing of this material relies on the Customer, who is also responsible for determining whether the material and the information in this document are appropriate for the Customer’s use.
Property | Test | Typical value | Units |
---|---|---|---|
Melt Flow Index (MFI) | ISO 1133 (190 °C / 2.16 kg) | 9 - 11 | g/10 min |
Density | ISO 1183 | 0.91 – 0.92 | g/cm3 |
Shore D hardness | ISO 868 | 61 - 63 | - |
Property | Test | Typical value | Units |
---|---|---|---|
Tensile Modulus | ISO 527-2/1A/1 | 1,050 – 1,150 | MPa |
Resistance at the tensile yield point | ISO 527-2/1A/50 | 23 - 25 | MPa |
Elongation at break to traction | ISO 527-2/1A/50 | > 20 | % |
Impact resistance Charpy with notch (23ºC) | ISO 179-1/1eA | > 3.5 | kJ/m2 |
All properties, except MFI tests, are conducted on ISO type 1-A injection moulded test specimens.
Typical Values are representative mean values.
This product is a recycled grade. Although raw materials are regular and homogeneous, material properties and/or performance may vary. Hence, values indicated in this datasheet are not to be construed as specifications. They are provided in good faith, but no guarantees are given and no responsibility is assumed by Polymer Recycling Labs, S.L. for the information in this document, which is accurate and reliable as of the date of publication.
The responsibility for safe and legal use, handling and processing of this material relies on the Customer, who is also responsible for determining whether the material and the information in this document are appropriate for the Customer’s use.
Property | Test | Typical value | Units |
---|---|---|---|
Melt Flow Index (MFI) | ISO 1133 (190 °C / 2,16 kg) | 4 - 5 | g/10 min |
Density | ISO 1183 | 0,99 - 1,00 | g/cm3 |
Shore D hardness | ISO 868 | 62 - 63 | - |
Property | Test | Typical value | Units |
---|---|---|---|
Tensile Modulus | ISO 527‐2/1A/1 | 1.200 - 1.300 | MPa |
Resistance at the tensile yield point | ISO 527‐2/1A/50 | 24 - 26 | MPa |
Elongation at break to traction | ISO 527‐2/1A/50 | > 300 | % |
Impact resistance Charpy with notch (23ºC) | ISO 179‐1/1eA | >3 | kJ/m2 |
- All properties, except MFI tests, are conducted on ISO type 1-A injection moulded test specimens.
- Typical Values are representative mean values.
This product is a recycled grade. Although raw materials are regular and homogeneous, material properties and/or performance may vary. Hence, values indicated in this datasheet are not to be construed as specifications. They are provided in good faith, but no guarantees are given and no responsibility is assumed by Polymer Recycling Labs, S.L. for the information in this document, which is accurate and reliable as of the date of publication.
The responsibility for safe and legal use, handling and processing of this material relies on the Customer, who is also responsible for determining whether the material and the information in this document are appropriate for the Customer’s use.
Property | Test | Typical value | Units |
---|---|---|---|
Melt Flow Index (MFI) | ISO 1133 (190 ºC / 2,16 kg) | 10,5 - 11,5 | g/10 min |
Density | ISO 1183 | 0,98 - 1,00 | g/cm3 |
Shore D hardness | ISO 868 | 62 - 63 | - |
Property | Test | Typical value | Units |
---|---|---|---|
Tensile Modulus | ISO 527-2/1A/1 | 1.350 - 1.450 | MPa |
Resistance at the tensile yield point | ISO 527-2/1A/50 | 24 - 26 | MPa |
Elongation at break to traction | ISO 527-2/1A/50 | >40 | % |
Impact resistance Charpy with notch (23ºC) | ISO 179-1/1eA | >3 | kJ/m2 |
- All properties, except MFI tests, are conducted on ISO type 1-A injection moulded test specimens.
- Typical Values are representative mean values.
Disclaimer:
This product is a recycled grade. Although raw materials are regular and homogeneous, material properties and/or performance may vary. Hence, values indicated in this datasheet are not to be construed as specifications. They are provided in good faith, but no guarantees are given and no responsibility is assumed by Polymer Recycling Labs, S.L. for the information in this document, which is accurate and reliable as of the date of publication.
The responsibility for safe and legal use, handling and processing of this material relies on the Customer, who is also responsible for determining whether the material and the information in this document are appropriate for the Customer’s use.
© 2018 POLYMER RECYCING LABS, S.L.
Property | Test | Typical value | Units |
---|---|---|---|
Melt Flow Index (MFI) | ISO 1133 (190 °C / 2,16 kg) | 10 - 12 | g/10 min |
Density | ISO 1183 | 1,00 - 1,02 | g/cm3 |
Shore D hardness | ISO 868 | 55 - 57 | - |
Property | Test | Typical value | Units |
---|---|---|---|
Tensile Modulus | ISO 527-2/1A/1 | 1.350 - 1.450 | MPa |
Resistance at the tensile yield point | ISO 527-2/1A/50 | 18 - 20 | MPa |
Elongation at break to traction | ISO 527-2/1A/50 | > 30 | % |
Impact resistance Charpy with notch (23ºC) | ISO 179-1/1eA | > 20 | kJ/m2 |
- All properties, except MFI tests, are conducted on ISO type 1-A injection moulded test specimens.
- Typical Values are representative mean values.
Disclaimer:
This product is a recycled grade. Although raw materials are regular and homogeneous, material properties and/or performance may vary. Hence, values indicated in this datasheet are not to be construed as specifications. They are provided in good faith, but no guarantees are given and no responsibility is assumed by Polymer Recycling Labs, S.L. for the information in this document, which is accurate and reliable as of the date of publication.
The responsibility for safe and legal use, handling and processing of this material relies on the Customer, who is also responsible for determining whether the material and the information in this document are appropriate for the Customer’s use.
© 2018 POLYMER RECYCING LABS, S.L.
Property | Test | Typical value | Units |
---|---|---|---|
Melt Flow Index (MFI) | ISO 1133 (190 ºC / 2,16 kg) | 9 - 11 | g/10 min |
Density | ISO 1183 | 1,09 - 1,11 | g/cm3 |
Shore D hardness | ISO 868 | 56 - 58 | - |
Property | Test | Typical value | Units |
---|---|---|---|
Tensile Modulus | ISO 527‐2/1A/1 | 1.800 - 1.900 | MPa |
Resistance at the tensile yield point | ISO 527‐2/1A/50 | 18 - 20 | MPa |
Elongation at break to traction | ISO 527‐2/1A/50 | >20 | % |
Impact resistance Charpy with notch (23ºC) | ISO 179-1/1eA | >15 | kJ/m2 |
- All properties, except MFI tests, are conducted on ISO type 1-A injection moulded test specimens.
- Typical Values are representative mean values.
Disclaimer:
This product is a recycled grade. Although raw materials are regular and homogeneous, material properties and/or performance may vary. Hence, values indicated in this datasheet are not to be construed as specifications. They are provided in good faith, but no guarantees are given and no responsibility is assumed by Polymer Recycling Labs, S.L. for the information in this document, which is accurate and reliable as of the date of publication.
The responsibility for safe and legal use, handling and processing of this material relies on the Customer, who is also responsible for determining whether the material and the information in this document are appropriate for the Customer’s use.
© 2018 POLYMER RECYCING LABS, S.L.
Property | Test | Typical value | Units |
---|---|---|---|
Melt Flow Index (MFI) | ISO 1133 (190ºC / 2,16 kg) | 3,5 - 4,5 | g/10 min |
Density | ISO 1183 | 0,94 - 0,96 | g/cm3 |
Shore D hardness | ISO 868 | 58 - 60 | - |
Property | Test | Typical value | Units |
---|---|---|---|
Tensile Modulus | ISO 527-2/1A/A | 800 - 900 | MPa |
Resistance at the tensile yield point | ISO 527-2/1A/50 | 22 - 24 | MPa |
Elongation at break to traction | ISO 527-2/1A/50 | >400 | % |
Impact resistance Charpy with notch (23ºC) | ISO 179-1/1eA | 4 - 5 | kJ/m2 |
- All properties, except MFI tests, are conducted on ISO type 1-A injection moulded test specimens.
- Typical Values are representative mean values.
Disclaimer:
This product is a recycled grade. Although raw materials are regular and homogeneous, material properties and/or performance may vary. Hence, values indicated in this datasheet are not to be construed as specifications. They are provided in good faith, but no guarantees are given and no responsibility is assumed by Polymer Recycling Labs, S.L. for the information in this document, which is accurate and reliable as of the date of publication.
The responsibility for safe and legal use, handling and processing of this material relies on the Customer, who is also responsible for determining whether the material and the information in this document are appropriate for the Customer’s use.
© 2018 POLYMER RECYCING LABS, S.L.
Property | Test | Typical value | Units |
---|---|---|---|
Melt Flow Index (MFI) | ISO 1133 (190º / 2,16 kg) | 0.3 - 0.7 | g/10 min |
Density | ISO 1183 | 0.94 - 0.96 | g/cm3 |
Shore D hardness | ISO 868 | 57 - 59 | - |
Property | Test | Typical value | Units |
---|---|---|---|
Tensile Modulus | ISO 527-2/1A/1 | 750 – 850 | MPa |
Resistance at the tensile yield point | ISO 527-2/1A/50 | 22 – 24 | MPa |
Elongation at break to traction | ISO 527-2/1A/50 | > 400 | % |
Impact resistance Charpy with notch (23ºC) | ISO 179-1/1eA | > 10 | kJ/m2 |
This product is a recycled grade. Although raw materials are regular and homogeneous, material properties and/or performance may vary. Hence, values indicated in this datasheet are not to be construed as specifications. They are provided in good faith, but no guarantees are given and no responsibility is assumed by Polymer Recycling Labs, S.L. for the information in this document, which is accurate and reliable as of the date of publication.
The responsibility for safe and legal use, handling and processing of this material relies on the Customer, who is also responsible for determining whether the material and the information in this document are appropriate for the Customer’s use.
Do not hesitate to contact us if you wish to launch a study of your current materials and learn about a specific development.